SA210C钢在涂覆不同质量比混合盐膜下的高温腐蚀行为
Corrosion Behavior of SA210C Steel Beneath Deposit Film of Mixed Salts Na2SO4-NaCl in Air at 600oC
SA210C钢在涂覆不同质量比混合盐膜下的高温腐蚀行为 |
| 占阜元, 刘宣义, 黄世福, 刘帅岐, 徐媛媛, 潘喜桂, 何华林, 刘光明 |
|
Corrosion Behavior of SA210C Steel Beneath Deposit Film of Mixed Salts Na2SO4-NaCl in Air at 600oC |
| ZHAN Fuyuan, LIU Xuanyi, HAUNG Shifu, LIU Shuaiqi, XU Yuanyuan, PAN Xigui, HE Hualin, LIU Guangming |
| 图6 涂覆不同质量比混合盐膜SA210C钢在600℃腐蚀10 h后截面微观形貌及能谱图 |
| Fig.6 Microscopic morphologies (a-c) of the cross sections of SA210C steel coated with mixedsalt films of Na2SO4∶NaCl = 3∶1 (a), 1∶1 (b), 1∶3 (c) after corrosion for 10 h at 600oC, and EDS analysis result of the box region marked in Fig.6c (d) |
|
|