SA210C钢在涂覆不同质量比混合盐膜下的高温腐蚀行为
Corrosion Behavior of SA210C Steel Beneath Deposit Film of Mixed Salts Na2SO4-NaCl in Air at 600oC
SA210C钢在涂覆不同质量比混合盐膜下的高温腐蚀行为 |
| 占阜元, 刘宣义, 黄世福, 刘帅岐, 徐媛媛, 潘喜桂, 何华林, 刘光明 |
|
Corrosion Behavior of SA210C Steel Beneath Deposit Film of Mixed Salts Na2SO4-NaCl in Air at 600oC |
| ZHAN Fuyuan, LIU Xuanyi, HAUNG Shifu, LIU Shuaiqi, XU Yuanyuan, PAN Xigui, HE Hualin, LIU Guangming |
| 图3 涂覆不同质量比混合盐膜SA210C钢在600℃腐蚀10 h后XRD图谱 |
| Fig.3 XRD patterns of SA210C steel coated with mixed salt films of different mass ratios after corrosion for 10 h at 600oC |
|
|