两种热处理状态的镍基单晶高温合金在900℃下(Na2SO4 + NaCl)混合盐中热腐蚀行为研究
Hot Corrosion Behavior of a Nickel Based Single Crystal High Temperature Alloy Subjected to Different Heat Treatments
两种热处理状态的镍基单晶高温合金在900℃下(Na2SO4 + NaCl)混合盐中热腐蚀行为研究 |
| 张金龙, 付广艳, 宁礼奎, 刘恩泽, 谭政, 佟健, 郑志 |
|
Hot Corrosion Behavior of a Nickel Based Single Crystal High Temperature Alloy Subjected to Different Heat Treatments |
| ZHANG Jinlong, FU Guangyan, NING Likui, LIU Enze, TAN Zheng, TONG Jian, ZHENG Zhi |
| 图6 两种热处理状态的镍基单晶高温合金在900℃热腐蚀不同时间后的宏观形貌 |
| Fig.6 Macro morphologies of CH (a-e) and CH-LA (f-j) alloy samples after hot corrosion in mixed molten salt at 900oC for 20 h (a, f), 40 h (b, g), 60 h (c, h), 80 h (d, i) and 100 h (e, j) |
|
|