同成分的超细贝氏体钢和Q&P钢在海水中应力腐蚀开裂行为对比研究
Comparative Study on Stress Corrosion Cracking Behavior of Ultrafine Bainitic Steel and Q&P Steel with Same Composition in Seawater
同成分的超细贝氏体钢和Q&P钢在海水中应力腐蚀开裂行为对比研究 |
| 苏志诚, 张弦, 程焱, 刘静, 吴开明 |
|
Comparative Study on Stress Corrosion Cracking Behavior of Ultrafine Bainitic Steel and Q&P Steel with Same Composition in Seawater |
| SU Zhicheng, ZHANG Xian, CHENG Yan, LIU Jing, WU Kaiming |
| 图12 2种实验钢在空气与模拟海水中断口剖面裂纹EBSD图 |
| Fig.12 EBSD images of fracture profile cracks of ultrafine bainite steel (a, c) and Q&P steel (b, d) in air (a, b) and 3.5%NaCl solution (c, d) |
|
|