T2铜合金和Q235钢在模拟北山地下水环境中的电偶腐蚀行为研究
Galvanic Corrosion of T2 Cu-alloy and Q235 Steel in Simulated Beishan Groundwater Environment
T2铜合金和Q235钢在模拟北山地下水环境中的电偶腐蚀行为研究 |
| 庞洁, 刘相局, 刘娜珍, 侯保荣 |
|
Galvanic Corrosion of T2 Cu-alloy and Q235 Steel in Simulated Beishan Groundwater Environment |
| PANG Jie, LIU Xiangju, LIU Nazhen, HOU Baorong |
| 图8 Q235钢在25℃下面积比为10∶1以及Cl-浓度为0.05 mol·L-1条件下溶液中电偶腐蚀48 h后的表面Raman光谱 |
| Fig.8 Raman spectra of inner layer (a, b) and out layer (c, d) of corrosion products formed on Q235 steel after galvanic corrosion, at 25oC with [Cl-] = 0.05 mol·L-1, Cu/carbon steel area ratio = 10∶1 |
|
|