潮湿空气中应力耦合固态NaCl作用下GH4169合金的中温腐蚀行为研究
Corrosion Behavior of GH4169 Alloy Under Flexural Tensile Stress and Beneath a NaCl Deposit Film in Water Vapor Containing Air at 600oC
潮湿空气中应力耦合固态NaCl作用下GH4169合金的中温腐蚀行为研究 |
| 王文泉, 崔宇, 薛蕴鹏, 刘莉, 王福会 |
|
Corrosion Behavior of GH4169 Alloy Under Flexural Tensile Stress and Beneath a NaCl Deposit Film in Water Vapor Containing Air at 600oC |
| WANG Wenquan, CUI Yu, XUE Yunpeng, LIU Li, WANG Fuhui |
| 图8 表面沉积NaCl的GH4169合金在潮湿的600℃环境下受不同应力载荷影响腐蚀20 h后的截面形貌 |
| Fig.8 Cross-sectional morphologies of NaCl-deposited GH4169 alloys treated by standard heat treatment (a-c) and solution heat treatment (d-f) after corrosion in a humid 600oC environment for 20 h under a stress load of 0 MPa (a, d), 600 MPa (b, e) and 800 MPa (c, f) |
|
|