Fe34Cr30Mo15Ni15Nb3Al3 高熵合金在500℃下氧含量为10-6%的液态铅铋合金中腐蚀行为研究 |
||||||||||||
| 潘宗宇, 刘静, 姜志忠, 罗林, 贾寒冰, 刘欣雨 | ||||||||||||
|
Corrosion Behavior of Fe34Cr30Mo15Ni15Nb3Al3 High-entropy Alloy in Molten Pb-Bi Eutectic Containing 10-6% Oxygen at 500oC |
||||||||||||
| PAN Zongyu, LIU Jing, JIANG Zhizhong, LUO Lin, JIA Hanbing, LIU Xinyu | ||||||||||||
| 表3 不同腐蚀时间氧化层的厚度 |
||||||||||||
| Table 3 Thickness of oxide layer for different corrosion times (µm) |
||||||||||||
|
||||||||||||