裂变产物碲致高镍合金GH3535晶间腐蚀研究

杜鑫, 杜乾, 苏钲雄, 郭少强, 王盛

Intergranular Corrosion of High Temperature Ni-based Alloy GH3535 Induced by Fission Product Tellurium

DU Xin, DU Qian, SU Zhengxiong, GUO Shaoqiang, WANG Sheng

图6 GH3535合金试样在10 mg/cm2 Te 条件下高温暴露后的TEM像及EDS元素面分布与高分辨图

Fig.6 TEM image (a), EDS element mappings (b-f) of GH3535 alloy after corrosion in 10 mg/cm2 Te at 700oC, HRTEM image of the selective area marked by yellow square in Fig.6a (g), and the corresponding fast-Fourier transform pattern (h)