裂变产物碲致高镍合金GH3535晶间腐蚀研究
Intergranular Corrosion of High Temperature Ni-based Alloy GH3535 Induced by Fission Product Tellurium
裂变产物碲致高镍合金GH3535晶间腐蚀研究 |
| 杜鑫, 杜乾, 苏钲雄, 郭少强, 王盛 |
|
Intergranular Corrosion of High Temperature Ni-based Alloy GH3535 Induced by Fission Product Tellurium |
| DU Xin, DU Qian, SU Zhengxiong, GUO Shaoqiang, WANG Sheng |
| 图3 GH3535合金试样在1, 6和10 mg/cm2 Te条件下高温暴露后截面SEM像及EDS元素面分布图 |
| Fig.3 SEM image and EDS element mappings of GH3535 Ni-based alloy after corrosion in 1 mg/cm2 (a), 6 mg/cm2 (b) and 10 mg/cm2 (c) Te at 700oC |
|
|