中性水系锌离子电池负极缓蚀剂研究进展
吴浩天, 张天遂, 李广芳, 刘宏芳

Corrosion Inhibitor for Zn Anode of Neutral Aqueous Zinc Ion Batteries
WU Haotian, ZHANG Tiansui, LI Guangfang, LIU Hongfang
表2 不同缓蚀剂的Zn||Zn对称电池循环性能统计对比表
Table 2 Cycling performance of Zn||Zn symmetric cells with corrosion inhibitor used in recent research
Corrosion inhibitorElectrolytesCurrent density, capacity and cycle timeRef.
dimethyl sulfoxideZnSO4

1 mA·cm-2, 1 mAh·cm-2, 2100 h

3 mA·cm-2, 3 mAh·cm-2, 200 h

[22]
N-methyl-2-pyrrolidoneZnSO41 mA·cm-2, 1 mAh·cm-2, 540 h[29]
ethylene glycolZnSO4

0.5 mA·cm-2, 0.5 mAh·cm-2, 1300 h

5 mA·cm-2, 0.5 mAh·cm-2, 800 h

[24]
triethylmethyl ammoniumZnCl2

1 mA·cm-2, 0.5 mAh·cm-2, 2145 h

5 mA·cm-2, 2.5 mAh·cm-2, 500 h

[40]
melamineZnSO42 mA·cm-2, 2 mAh·cm-2, 3000 h[42]
monosodium glutamateZnSO4

2 mA·cm-2, 2 mAh·cm-2, 2200 h

5 mA·cm-2, 5 mAh·cm-2, 1700 h

[43]
glycineZnSO4

1 mA·cm-2, 0.5 mAh·cm-2, 2000 h

4 mA·cm-2, 2 mAh·cm-2, 600 h

[44]
histidineZnSO42 mA·cm-2, 1 mAh·cm-2, 4180 h[45]
L-cysteineZnSO41 mA·cm-2, 0.5 mAh·cm-2, 2500 h[46]
SeO2ZnSO42 mA·cm-2, 2 mAh·cm-2, 2100 h[55]
sucroseZnSO4

1 mA·cm-2, 1 mAh·cm-2, 2000 h

2 mA·cm-2, 2 mAh·cm-2, 500 h

[57]
sorbitolZnSO41 mA·cm-2, 0.5 mAh·cm-2, 2000 h[60]
alkyl polyglucosideZnSO41 mA·cm-2, 0.25 mAh·cm-2, 4000 h[61]
silk peptideZnSO41 mA·cm-2, 1 mAh·cm-2, 3000 h[64]
polyaspartic acidZnSO40.5 mA cm-2, 0.5 mAh·cm-2, 3200 h[65]
ovalbuminZnSO41 mA·cm-2, 1 mAh·cm-2, 2200 h[71]
γ-valerolactoneZnSO41 mA·cm-2, 1 mAh·cm-2, 3500 h[72]
AgNO3ZnSO40.5 mA·cm-2, 0.25 mAh·cm-2, 1800 h[73]
KIZnSO41 mA·cm-2, 1 mAh·cm-2, 3000 h[74]
Ni2+ZnSO41 mA·cm-2, 1 mAh·cm-2, 900 h[75]
cholinium cationsZnSO41 mA·cm-2, 1 mAh·cm-2, 2000 h[76]
dioxaneZnSO41 mA·cm-2, 1 mAh·cm-2, 2000 h[77]
sodium tartrateZnSO40.5 mA·cm-2, 0.25 mAh·cm-2, 1500 h[78]
tetramethylureaZn(OTf)21 mA·cm-2, 1 mAh·cm-2, 3000 h[79]
thioureaZnSO41 mA·cm-2, 1 mAh·cm-2, 1200 h[80]
tetrahydrofuranZnSO4

0.5 mA·cm-2, 0.5 mAh·cm-2, 1300 h

1 mA·cm-2, 1 mAh·cm-2, 500 h

[81]
phytic acidZnSO41 mA·cm-2, 1 mAh·cm-2, 1200 h[82]
penta-potassium triphosphateZnSO41 mA·cm-2, 1 mAh·cm-2, 3800 h[83]
1-hydroxy ethylidene-1,1-diphosphonic acidZnSO41 mA·cm-2, 1 mAh·cm-2, 1500 h[84]
taurineZnSO41 mA·cm-2, 1 mAh·cm-2, 3000 h[85]
tetrabutylammonium 4-toluenesulfonateZn(PS)21 mA·cm-2, 1 mAh·cm-2, 2000 h[86]
1-phenylethylamine hydrochlorideZnSO41 mA·cm-2, 1 mAh·cm-2, 2082 h[87]
succinimideZnSO420 mA·cm-2, 10 mAh·cm-2, 680 h[88]
hexamethylenetetramineZnSO45 mA·cm-2, 1 mAh·cm-2, 4000 h[89]
1-ethyl-3-methylimidazolium chlorideZnSO41 mA·cm-2, 1 mAh·cm-2, 500 h[90]
1-butyl-3-methylimidazolium cationZnSO4

2 mA·cm-2, 1 mAh·cm-2, 3162 h

5 mA·cm-2, 5 mAh·cm-2, 1410 h

10 mA·cm-2, 10 mAh·cm-2, 1000 h

[91]
L-ascorbic acid sodiumZnSO41 mA·cm-2, 1 mAh·cm-2, 1200 h[92]