奥氏体钢辐照促进应力腐蚀开裂行为机制的研究进展
Research Progress on Irradiation Assisted Stress Corrosion Cracking Behavior and Mechanism of Austenitic Steel
奥氏体钢辐照促进应力腐蚀开裂行为机制的研究进展 |
| 高俊宣, 曹晗, 匡文军, 郑全, 张鹏, 钟巍华 |
|
Research Progress on Irradiation Assisted Stress Corrosion Cracking Behavior and Mechanism of Austenitic Steel |
| GAO Junxuan, CAO Han, KUANG Wenjun, ZHENG Quan, ZHANG Peng, ZHONG Weihua |
| 图7 微观缺陷与力学性能随退火条件的变化[ |
| Fig.7 Variation of microscopic defects and mechanical properties with annealing conditions: (a) size and number density of dislocation loops in 304L stainless steel irradiated to 5.9 dpa under different annealing conditions[ |
|
|