IN625激光熔覆层腐蚀致微裂纹扩展机理研究
Prpogation Mechanism of Microcracks Caused by Corrosion of Laser Cladded In625 Coating on Nodular Cast Iron in 3.5%NaCl Solution
IN625激光熔覆层腐蚀致微裂纹扩展机理研究 |
| 邓双九, 李昌, 余梦辉, 韩兴 |
|
Prpogation Mechanism of Microcracks Caused by Corrosion of Laser Cladded In625 Coating on Nodular Cast Iron in 3.5%NaCl Solution |
| DENG Shuangjiu, LI Chang, YU Menghui, HAN Xing |
| 图19 沿数据提取线获得不同时间离子浓度变化曲线图 |
| Fig.19 Variations of Ni2+ (a, b), Na+ (c, d), and Cl- (e, f) concentrations with time at the center line position (a, c, e) and edge line position (b, d, f) of the microcrack |
|
|