组织老化对P92钢在超临界水中氧化行为影响研究

於琛钧, 张天翼, 张乃强, 朱忠亮

Influence of Thermal Aging on Corrosion Behavior of Ferritic-martensitic Steel P92 in Supercritical Water

YU Chenjun, ZHANG Tianyi, ZHANG Naiqiang, ZHU Zhongliang

图10 P92钢在超临界水中氧化1500 h后氧化膜截面形貌和EDS线扫

Fig.10 Cross-sectional morphologies (a-c) and EDS line scannings (d-f) along the white lines for P92 steel aged for 0 h (a, d), 200 h (b, e) and 400 h (c, f) and then oxidized in SCW for 1500 h