A100钢在动态薄液膜和人工海水环境中的应力腐蚀行为对比研究
Comparative Study on Stress Corrosion Behavior of A100 Ultrahigh-strength Steel Beneath Dynamic Thin Electrolyte Layer and in Artificial Seawater Environments
A100钢在动态薄液膜和人工海水环境中的应力腐蚀行为对比研究 |
| 郭昭, 李晗, 崔中雨, 王昕, 崔洪芝 |
|
Comparative Study on Stress Corrosion Behavior of A100 Ultrahigh-strength Steel Beneath Dynamic Thin Electrolyte Layer and in Artificial Seawater Environments |
| GUO Zhao, LI Han, CUI Zhongyu, WANG Xin, CUI Hongzhi |
| 图9 A100钢在空气、人工海水和薄液膜中的断口微观形貌 |
| Fig.9 Fracture morphologies of service state A100 steel in air (a1-a3), ASW (b1-b3) and TEL (c1-c3) |
|
|