A100钢在动态薄液膜和人工海水环境中的应力腐蚀行为对比研究
Comparative Study on Stress Corrosion Behavior of A100 Ultrahigh-strength Steel Beneath Dynamic Thin Electrolyte Layer and in Artificial Seawater Environments
A100钢在动态薄液膜和人工海水环境中的应力腐蚀行为对比研究 |
| 郭昭, 李晗, 崔中雨, 王昕, 崔洪芝 |
|
Comparative Study on Stress Corrosion Behavior of A100 Ultrahigh-strength Steel Beneath Dynamic Thin Electrolyte Layer and in Artificial Seawater Environments |
| GUO Zhao, LI Han, CUI Zhongyu, WANG Xin, CUI Hongzhi |
| 图8 A100钢在两种腐蚀环境中应力-应变曲线和以伸长率损失为指标的SCC敏感性 |
| Fig.8 Stress-strain curves (a) and SCC susceptibility based on elongation loss (b) of A100 steel in the two environments |
|
|