加载条件对镍基617合金在超临界水中腐蚀疲劳裂纹扩展速率的影响
Effect of Different Loading Conditions on Corrosion Fatigue Crack Growth Rate of Nickel Base Alloy 617 in Supercritical Water
加载条件对镍基617合金在超临界水中腐蚀疲劳裂纹扩展速率的影响 |
| 陈震宇, 朱忠亮, 马辰昊, 张乃强, 刘宇桐 |
|
Effect of Different Loading Conditions on Corrosion Fatigue Crack Growth Rate of Nickel Base Alloy 617 in Supercritical Water |
| CHEN Zhenyu, ZHU Zhongliang, MA Chenhao, ZHANG Naiqiang, LIU Yutong |
| 图7 Inconel 617的CFCGR随th的变化 |
| Fig.7 CFCGR of Inconel 617 under two holding time conditions |
|
|