液膜厚度对固态超滑表面在薄液膜下腐蚀行为的影响

任黄威, 廖伯凯, 崔琳晶, 项腾飞

Effect of Liquid Film Thickness on Corrosion Behavior of Solid Slippery Surface under Thin Liquid Film

REN Huangwei, LIAO Bokai, CUI Linjing, XIANG Tengfei

表1 SSS在各液膜厚度下不同浸泡时间的电化学参数

Table 1 Electrochemical parameters of the SSS with different soaking times at different liquid film thicknesses

Thickness / μm t / d R1 / Ω·cm2 Q1 / F·cm2 n1 R2 / Ω·cm2 Q2 / F·cm2 n2 R3 / Ω·cm2 W / Ω·cm2 500 1 58.87 2.12×10-6 0.77 2.18×103 3.45×10-6 0.45 8.30×105 - 2 59.78 6.17×10-6 0.75 1.34×103 7.20×10-6 0.53 8.08×105 - 4 59.31 8.66×10-6 0.73 1.17×103 1.03×10-6 0.61 7.84×105 - 7 61.50 1.03×10-6 0.74 1.02×103 4.58×10-6 0.46 7.41×105 - 250 1 88.48 5.82×10-6 0.89 2.56×103 2.37×10-6 0.47 1.61×106 - 2 89.61 2.65×10-6 0.80 1.74×103 1.66×10-5 0.36 5.05×105 - 4 90.49 1.20×10-5 0.79 1.48×103 3.11×10-5 0.49 3.26×105 - 7 92.57 3.76×10-5 0.83 1.39×103 4.93×10-5 0.35 7.79×104 - 100 1 130.6 2.88×10-6 0.82 1.54×105 5.24×10-6 0.78 3.68×106 - 2 130.5 4.07×10-6 0.82 8.92×104 3.70×10-6 0.69 3.67×106 - 4 133.1 5.78×10-6 0.78 8.53×104 2.72×10-5 0.48 1.16×106 - 7 134.6 1.01×10-5 0.72 6.98×104 2.44×10-5 0.69 6.49×105 - 50 1 157.4 2.57×10-6 0.78 7.53×103 1.72×10-6 0.62 7.06×105 2.86×10-5 2 158.5 7.25×10-6 0.76 6.32×103 1.50×10-6 0.37 5.21×105 3.27×10-5 4 159.2 8.78×10-6 0.79 4.69×103 2.42×10-5 0.35 1.54×105 3.69×10-5 7 159.9 9.46×10-5 0.80 3.13×103 1.10×10-5 0.38 5.29×104 4.44×10-5