高温下L80钢的断裂机理及CO2/H2S模拟工况下的腐蚀行为
Tensile Property of L80 Steel in Air at 25-350 ℃ and Its Corrosion Behavior in Simulated Casing Service Conditions at 150-350 ℃
高温下L80钢的断裂机理及CO2/H2S模拟工况下的腐蚀行为 |
| 周志平, 吴大康, 张宏福, 张磊, 李明星, 张志鑫, 钟显康 |
|
Tensile Property of L80 Steel in Air at 25-350 ℃ and Its Corrosion Behavior in Simulated Casing Service Conditions at 150-350 ℃ |
| ZHOU Zhiping, WU Dakang, ZHANG Hongfu, ZHANG Lei, LI Mingxing, ZHANG Zhixin, ZHONG Xiankang |
| 图7 L80钢在不同温度下腐蚀7 d后试样的宏观形貌 |
| Fig.7 Macro morphologies of L80 steel before and after 7 d corrosion at different temperatures |
|
|