高温下L80钢的断裂机理及CO2/H2S模拟工况下的腐蚀行为
Tensile Property of L80 Steel in Air at 25-350 ℃ and Its Corrosion Behavior in Simulated Casing Service Conditions at 150-350 ℃
高温下L80钢的断裂机理及CO2/H2S模拟工况下的腐蚀行为 |
| 周志平, 吴大康, 张宏福, 张磊, 李明星, 张志鑫, 钟显康 |
|
Tensile Property of L80 Steel in Air at 25-350 ℃ and Its Corrosion Behavior in Simulated Casing Service Conditions at 150-350 ℃ |
| ZHOU Zhiping, WU Dakang, ZHANG Hongfu, ZHANG Lei, LI Mingxing, ZHANG Zhixin, ZHONG Xiankang |
| 图6 不同温度下L80钢在模拟工况中的腐蚀速率 |
| Fig.6 Corrosion rates of L80 steel in the simulated conditions with different temperatures |
|
|