F22母材与焊缝在模拟沿海空气中的高温腐蚀行为研究
High Temperature Corrosion Behavior of F22 Base Metal and Weld in Simulated Coastal Atmosphere
F22母材与焊缝在模拟沿海空气中的高温腐蚀行为研究 |
| 柳志浩, 刘光明, 何思凡, 董猛, 李玉, 李富天, 祝婷 |
|
High Temperature Corrosion Behavior of F22 Base Metal and Weld in Simulated Coastal Atmosphere |
| LIU Zhihao, LIU Guangming, HE Sifan, DONG Meng, LI Yu, LI Futian, ZHU Ting |
| 图4 F22母材与焊缝在510 ℃模拟沿海空气中腐蚀3000 h的腐蚀动力学曲线与拟合曲线 |
| Fig.4 Corrosion kinetics (a) and fitting (b) curves of F22 base metal and weld joint during exposure at 510 ℃ for 3000 h in simulating coastal air |
|
|