“高温-结盐-CO2/O2”多因素耦合环境下热浸铝镀层腐蚀行为研究
Corrosion Behavior of Hot-dip Aluminum Coating in “High Temperature-salt Deposited-CO2/O2” Multi-degree Coupling Environment
“高温-结盐-CO2/O2”多因素耦合环境下热浸铝镀层腐蚀行为研究 |
| 陈庆国, 唐全宏, 秦振杰, 李一凡, 李磊, 李轩鹏, 袁军涛, 苏航, 付安庆 |
|
Corrosion Behavior of Hot-dip Aluminum Coating in “High Temperature-salt Deposited-CO2/O2” Multi-degree Coupling Environment |
| CHEN Qingguo, TANG Quanhong, QIN Zhenjie, LI Yifan, LI Lei, LI Xuanpeng, YUAN Juntao, SU Hang, FU Anqing |
| 图3 热浸铝镀层在高温高压模拟实验前后以及20#钢在实验后的XRD图谱 |
| Fig.3 XRD patterns of HDA coating (a) and 20# steel (b) before/after and after high-temperature-high-pressure simulation test, respectively |
|
|