晶粒尺寸对304L奥氏体不锈钢氢脆的影响

王艳飞, 李耀州, 黄玉婷, 谢宏琳, 吴炜杰

Effect of Grain Size on Hydrogen Embrittlement of 304L Austenitic Stainless Steel

WANG Yanfei, LI Yaozhou, HUANG Yuting, XIE Honglin, WU Weijie

表1 不同退火处理试样的平均晶粒尺寸、αʹ马氏体含量和位错密度

Table 1 Mean grain size, αʹ martensite content and dislocation density of specimens annealed by different parameters

Specimen TA / ℃ tA / min d / μm Vαʹ / % ρd / m-3 AT700-5 700 5 1.3 16.1 1.2×1014 AT800-20 800 20 3.7 6.6 4.2×1013 AT900-20 900 20 14.3 1.8 3.7×1013 AT1050-20 1050 20 35.0 0.89 4.2×1013