690 MPa级耐候桥梁钢焊接接头在模拟工业大气环境下的耐蚀性研究
Corrosion Behavior of Weld Joint of 690 MPa Weathering Bridge Steel in Simulated Industrial Atmosphere
690 MPa级耐候桥梁钢焊接接头在模拟工业大气环境下的耐蚀性研究 |
| 程鹏, 刘静, 牟文广, 黄峰, 黄先球, 庞涛 |
|
Corrosion Behavior of Weld Joint of 690 MPa Weathering Bridge Steel in Simulated Industrial Atmosphere |
| CHENG Peng, LIU Jing, MU Wenguang, HUANG Feng, HUANG Xianqiu, PANG Tao |
| 图10 焊接接头不同区域腐蚀不同时间后的|Z|0.01 Hz值 |
| Fig.10 Low-frequency impedances at 0.01 Hz for the different zones of weld joint after corrosion for different time |
|
|