温度对钛合金应力腐蚀行为的影响
李文桔, 张慧霞, 张宏泉, 郝福耀, 仝宏韬

Effect of Temperature on Stress Corrosion Behavior of Ti-alloy Ti80 in Sea Water
LI Wenju, ZHANG Huixia, ZHANG Hongquan, HAO Fuyao, TONG Hongtao
表1 Ti80钛合金样品应力腐蚀开裂数据
Table 1 Stress corrosion cracking parameters of Ti80 Ti-alloy in seawater at different temperatures
T / ℃Crack length mm

K1SCC

MPa·m0.5

Crack growth rate m·s-1
56.99356.372.310×10-9
154.61664.631.526×10-9
253.96866.841.312×10-9
353.39575.691.123×10-9