三元Co-Ni-Al合金在800~1000 ℃纯氧中的氧化行为研究 |
|||||||||
任延杰, 吕云蕾, 戴汀, 郭晓慧, 陈荐, 周立波, 邱玮, 牛焱 | |||||||||
Oxidation Behavior of Ternary Alloys Co-20Ni-3Al and Co-20Ni-5Al in 105 Pa O2 Atmosphere at 800-1000 ℃ |
|||||||||
REN Yanjie, LV Yunlei, DAI Ting, GUO Xiaohui, CHEN Jian, ZHOU Libo, QIU Wei, NIU Yan | |||||||||
表1 两种Co-20Ni-Al合金的设计成分和由ICP光谱技术测得的实际成分 |
|||||||||
Table 1 Nominal and ICP-OES determined compositions of Co-20Ni-3Al and Co-20Ni-5Al alloys |
|||||||||
|
|||||||||