干湿比对CrNiMoV钢在120 mmol/L NH4H2PO4溶液中电化学腐蚀行为的影响 |
王通, 孟惠民, 郭维华, 葛鹏飞, 巩秀芳, 倪荣, 龚显龙, 戴君, 隆彬, 李全德 |
Influence of Dry-wet Ratio on Electrochemical Corrosion Behavior of CrNiMoV Steel in 120 mmol/L NH4H2PO4 Solution |
WANG Tong, MENG Huimin, GUO Weihua, GE Pengfei, GONG Xiufang, NI Rong, GONG Xianlong, DAI Jun, LONG Bin, LI Quande |
图8 1R钢和2R钢在不同浸泡条件实验21 d后的开路电位 |
Fig.8 Open circuit potentials of 1R steel (a) and 2R steel (b) aftertest under different immersion conditions for 21 d |