交变压力对无溶剂环氧涂层在模拟超深海环境下的电化学行为
|
王腾宇, 张正贵, 陆卫中, 吴希革
|
Effect of Alternating Pressure on Electrochemical Behavior of Solvent-free Epoxy Coating in Simulated Ultra-deep Sea Environment
|
WANG Tengyu, ZHANG Zhenggui, LU Weizhong, WU Xige
|
|
表1 涂层A在0.1~30 MPa交变压力下浸泡480 h期间EIS参数拟合结果
|
Table 1 Fitting results of EIS parameters of epoxy powder coating during 480 h immersion at 0.1-30 MPa alternating pressure
|
|
Time / h | Rc / Ω·cm2 | n1 | Qc / F·cm-2 | Rct / Ω·cm2 | n2 | Qdl / F·cm-2 | Zw |
---|
6 | 3.287×1011 | 0.9 | 2.291×10-10 | --- | --- | --- | --- | 28 | 4.258×1010 | 0.9492 | 2.324×10-10 | --- | --- | --- | --- | 41 | 4.43×1010 | 0.9477 | 2.37×10-10 | --- | --- | --- | --- | 52 | 3.909×1010 | 0.9441 | 2.486×10-10 | --- | --- | --- | --- | 75 | 2.556×1010 | 0.9 | 2.914×10-10 | --- | --- | --- | --- | 144 | 1.896×1010 | 0.9365 | 2.739×10-10 | --- | --- | --- | --- | 240 | 1.138×109 | 0.954 | 2.943×10-10 | 1.386×1010 | 0.9676 | 3.81×10-10 | --- | 360 | 1.49×108 | 0.3122 | 3.954×10-10 | 3.07×109 | 0.3122 | 3.125×10-9 | --- | 480 | 4.447×107 | 0.8951 | 5.105×10-10 | 1.835×108 | 0.4922 | 6.488×10-9 | --- |
|
|
|