CO2-H2S-Cl-共存的地层水环境中Cr含量对钢的腐蚀产物膜特性的影响
Influence of Cr Content on Characteristics of Corrosion Product Film Formed on Several Steels in Artifitial Stratum Waters Containing CO2-H2S-Cl-
CO2-H2S-Cl-共存的地层水环境中Cr含量对钢的腐蚀产物膜特性的影响 |
| 王小红, 李子硕, 唐御峰, 谭浩, 蒋焰罡 |
|
Influence of Cr Content on Characteristics of Corrosion Product Film Formed on Several Steels in Artifitial Stratum Waters Containing CO2-H2S-Cl- |
| WANG Xiaohong, LI Zishuo, TANG Yufeng, TAN Hao, JIANG Yangang |
| 图8 L80Cr13钢在模拟地层水中浸泡14 d后的侧面形貌、EDS线扫描分析结果及正面微观形貌 |
| Fig.8 Cross-sectional SEM topography (a), EDS line scanning results (b) and microscopic morphology (c) of L80Crl3 steel after immersion in the simulated stratum water for 14 d |
|
|