CO2-H2S-Cl-共存的地层水环境中Cr含量对钢的腐蚀产物膜特性的影响
Influence of Cr Content on Characteristics of Corrosion Product Film Formed on Several Steels in Artifitial Stratum Waters Containing CO2-H2S-Cl-
CO2-H2S-Cl-共存的地层水环境中Cr含量对钢的腐蚀产物膜特性的影响 |
| 王小红, 李子硕, 唐御峰, 谭浩, 蒋焰罡 |
|
Influence of Cr Content on Characteristics of Corrosion Product Film Formed on Several Steels in Artifitial Stratum Waters Containing CO2-H2S-Cl- |
| WANG Xiaohong, LI Zishuo, TANG Yufeng, TAN Hao, JIANG Yangang |
| 图3 L80和L80Cr13钢在模拟地层水中浸泡14 d后的CLSM形貌及其点蚀密度和平均深度 |
| Fig.3 CLSM images (a, d), pitting densities (b, e) and average depths (c, f) of L80 (a-c) and L80Cr13 (d-f) steels after immersion in the simulated solution for 14 d |
|
|