pH值对X100管线钢在CO32-/HCO3-溶液中的电化学与应力腐蚀行为的影响
Effect of pH on Electrochemical Corrosion and Stress Corrosion Behavior of X100 Pipeline Steel in CO32-/HCO3- Solutions
pH值对X100管线钢在CO32-/HCO3-溶液中的电化学与应力腐蚀行为的影响 |
| 李柯萱, 宋龙飞, 李晓荣 |
|
Effect of pH on Electrochemical Corrosion and Stress Corrosion Behavior of X100 Pipeline Steel in CO32-/HCO3- Solutions |
| LI Kexuan, SONG Longfei, LI Xiaorong |
| 图8 X100管线钢慢应变速率拉伸测试后的断口形貌 |
| Fig.8 Fracture morphologies of X100 pipeline steel after slow strain rate test in CO32-/HCO3- solutions with pH values of 8.55 (a), 9.62 (b), 10.58 (c) and 11.55 (d) |
|
|