预腐蚀工艺对Gd2Zr2O7陶瓷抗CMAS腐蚀性能的影响
Effect of Pre-corrosion of Gd2Zr2O7 at 900-1300 ℃ on Its Hot Corrosion Behavior at 1250 ℃ Beneath Deposites of CaO-MgO-Al2O3-SiO2
预腐蚀工艺对Gd2Zr2O7陶瓷抗CMAS腐蚀性能的影响 |
| 胡蕴媛, 钱伟, 花银群, 叶云霞, 蔡杰, 戴峰泽 |
|
Effect of Pre-corrosion of Gd2Zr2O7 at 900-1300 ℃ on Its Hot Corrosion Behavior at 1250 ℃ Beneath Deposites of CaO-MgO-Al2O3-SiO2 |
| HU Yunyuan, QIAN Wei, HUA Yinqun, YE Yunxia, CAI Jie, DAI Fengze |
| 图4 经不同温度预腐蚀的Gd2Zr2O7在1250 ℃下CMAS腐蚀3 h的反应层深度 |
| Fig.4 Thicknesses of the reaction layers formed on Gd2Zr2O7 pre-corroded at different temperatures after CMAS corrosion at 1250 ℃ for 3 h |
|
|