Cl-与HSO3-对建筑用439不锈钢腐蚀行为的影响

陈昊, 樊志彬, 陈志坚, 周学杰, 郑鹏华, 吴军

Effect of Cl- and HSO3- on Corrosion Behavior of 439 Stainless Steel Used in Construction

CHEN Hao, FAN Zhibin, CHEN Zhijian, ZHOU Xuejie, ZHENG Penghua, WU Jun

表3 电化学阻抗谱等效电路拟合参数

Table 3 Fitting parameters of EIS based on equivalent circuit

Solution / (mol·L-1) Rs / Ω·cm-2 Q1 / F·cm-2 n1 R1 / Ω·cm-2 Q2 / F·cm-2 n2 R2 / Ω·cm-2 0.62 NaCl 50.17 1.39×10-5 0.87 2.01×104 4.08×10-5 0.65 2.07×105 0.05 NaHSO3 485.70 1.82×10-5 0.91 4.01×104 1.37×10-5 0.45 7.55×105 0.10 NaHSO3 258.40 2.91×10-5 0.98 1.60×104 2.81×10-5 0.75 3.09×105 0.50 NaHSO3 64.09 2.11×10-5 0.37 1.36×104 2.52×10-5 0.90 2.95×105 (0.62+0.05) NaCl+NaHSO3 40.65 2.94×10-5 0.90 4.24×103 2.98×10-5 0.82 2.48×104 (0.62+0.10) NaCl+NaHSO3 38.86 2.41×10-5 0.91 8.15×103 3.37×10-5 0.60 3.21×104 (0.62+0.50) NaCl+NaHSO3 27.72 2.76×10-5 0.91 7.70×103 3.87×10-5 0.72 3.34×104