Corrosion Mechanism of Materials in Three Typical Harsh Marine Atmospheric Environments
CUI Zhongyu(), GE Feng, WANG Xin
), GE Feng, WANG Xin
图3. AZ31镁合金在西沙海洋大气环境下的腐蚀失重、点蚀深度变化以及纯锌锈层的形貌及EPMA元素分布结果[
Fig.3. Mass loss (a), pit depth variation (b) of AZ31 Mg-based alloy during exposure in Xisha marine atmosphere, and cross-sectional morphology and element mappings (c) of the corrosion product layer formed on pure Zn after exposure for 4 a[