Corrosion Mechanism of Materials in Three Typical Harsh Marine Atmospheric Environments
CUI Zhongyu(), GE Feng, WANG Xin
), GE Feng, WANG Xin
图1. Q235钢在南极中山站暴晒1个月后的腐蚀形貌、腐蚀产物Raman分析及表面深度分布
Fig.1. Macroscopic corrosion morphologies of the skyward (a) and backward (b) surfaces of Q235 steel sample after exposure in Zhongshan Station of the South Pole for 1 month, corrosion product morphology (c), pitting morphology (d), Raman analysis of the corrosion products (e), surface profile (f) and depth distributions (g, h)