轻合金锆/钛基转化膜的设计及性能研究
杨延格1(
), 曹京宜2, 王兴奇1, 方志刚2, 于宏飞1, 于宝兴1, 王福会3
), 曹京宜2, 王兴奇1, 方志刚2, 于宏飞1, 于宝兴1, 王福会3
Design and Performance of Zr- and/or Ti-based Chemical Conversion Coatings for Light Alloys
YANG Yange1(), CAO Jingyi2, WANG Xingqi1, FANG Zhigang2, YU Hongfei1, YU Baoxing1, WANG Fuhui3
), CAO Jingyi2, WANG Xingqi1, FANG Zhigang2, YU Hongfei1, YU Baoxing1, WANG Fuhui3
图2. 磷酸盐复合转化膜成膜不同时间的同步辐射图像[
Fig.2. Real-time X-ray phase-contrast images of a nano Al2O3/phosphate composite conversion coating formed in the presence of a magnetic field of 0.3 T (a~c), and a phosphate conversion coating formed in the absence of a magnetic field (d~f) after immersion time of 2 min (a, d), 5 min (b, e) and 8 min (c, f)[