Optimization of Titanate Modified Silane Coatings and Their Effect on Corrosion Resistance of 5056 Aluminum Foils
YU Shuaixian1, WU Yajun1, WU Haisheng2, WU Liang1, MA Yanlong3, DENG Shengwei4, SUN Lidong1()
)
图7. 铝箔样品宏观盐雾腐蚀后表面形貌
Fig.7. Photographs of various samples after salt spray tests for different durations: (a) 5056 aluminum foil, (b) anodic oxide film, (c) silane sealing coating (total solute content: 6%) and (d) silane/titanate sealing coating (total solute content: 6%, Ti:Si=0.3:5.7)