铝硅复合对Fe32Mn7Cr3Al2Si钢氧化改性层耐蚀性的影响
Corrosion Performance of Transition Layer at Interface of Oxide Scale/substrate Formed on Austenitic Steel Fe32Mn7Cr3Al2Si During High Temperature Oxidation
铝硅复合对Fe32Mn7Cr3Al2Si钢氧化改性层耐蚀性的影响 |
| 梁泰贺, 朱雪梅, 张振卫, 王新建, 张彦生 |
|
Corrosion Performance of Transition Layer at Interface of Oxide Scale/substrate Formed on Austenitic Steel Fe32Mn7Cr3Al2Si During High Temperature Oxidation |
| LIANG Taihe, ZHU Xuemei, ZHANG Zhenwei, WANG Xinjian, ZHANG Yansheng |
| 图3 Fe32Mn7Cr3Al2Si钢氧化层的XRD谱 |
| Fig.3 XRD patterns of Fe32Mn7Cr3Al2Si steel after cyclic oxidation at 700 and 800 ℃ in air |
|
|