超声冲击改善P355NL1钢焊接接头腐蚀疲劳性能研究
|
王永祥, 何柏林, 李力
|
Improvement of Corrosion Fatigue Performance of P355NL1 Steel Welded Joint by Ultrasonic Impact
|
WANG Yongxiang, HE Bolin, LI Li
|
|
表2 焊态试样在6%NaCl介质中的疲劳寿命
|
Table 2 Fatigue lifes of joint specimens in 6%NaClmedium
|
|
Sample number | Stress range | Cycle times | Fracture location |
---|
1 | 215 | 6.00×105 | Weld toe | 2 | 210 | 1.60×106 | Weld toe | 3 | 200 | 3.00×106 | Weld toe | 4 | 190 | 4.12×106 | Weld toe | 5 | 180 | 1.30×106 | Weld toe | 6 | 170 | 1.62×107 | Weld toe | 7 | 160 | 1.80×107 | Weld toe | 8 | 150 | 2.16×107 | Weld toe | 9 | 140 | 2.76×107 | Weld toe | 10 | 130 | 7.20×107 | Weld toe | 11 | 120 | 2.08×108 | Weld toe | 12 | 115 | 5.00×108 | Weld toe | 13 | 110 | 1.00×109 | Not broken |
|
|
|