不同组织的316L不锈钢在NH4Cl环境下应力腐蚀行为与机理
Stress Corrosion Cracking Behavior of 316L Stainless Steel with Varying Microstructure in Ammonium Chloride Environment
不同组织的316L不锈钢在NH4Cl环境下应力腐蚀行为与机理 |
| 孙宝壮, 周霄骋, 李晓荣, 孙玮潞, 刘子瑞, 王玉花, 胡洋, 刘智勇 |
|
Stress Corrosion Cracking Behavior of 316L Stainless Steel with Varying Microstructure in Ammonium Chloride Environment |
| SUN Baozhuang, ZHOU Xiaocheng, LI Xiaorong, SUN Weilu, LIU Zirui, WANG Yuhua, HU Yang, LIU Zhiyong |
| 图8 不同组织316L不锈钢在饱和NH4Cl沸腾溶液中裂纹沿厚度扩展SEM像 |
| Fig.8 SEM images of crack growth along the thickness of 316L stainless steel under different heat treatment in saturated NH4Cl boiling solution: (a) as-received microstructure, (b) solid-solution microstructure, (c) sensitized microstructure |
|
|