温度影响席夫碱缓蚀剂吸附的机理研究

胡慧慧, 陈长风

Mechanism of Temperature Influence on Adsorption of Schiff Base

HU Huihui, CHEN Changfeng

图4 N80钢在不同温度下添加BB-S和B-S缓蚀剂的腐蚀形貌

Fig.4 Corrosion morphologies of N80 steel after corrosion in 0.5 mol·L-1 HCl solutions containing BB-S (a1~a4) and B-S (b1~b4) inhibitors at 30 ℃ (a1, b1), 50 ℃ (a2, b2), 70 ℃ (a3, b3) and 90 ℃ (a4, b4)