Zn及锌锂合金在人工尿液中的腐蚀行为

陆黎立, 刘丽君, 姚生莲, 李华芳, 王鲁宁

Degradation Behavior of Pure Zinc and Zn-xLi Alloy in Artificial Urine

LU Lili, LIU Lijun, YAO Shenglian, LI Huafang, WANG Luning

表4 浸泡不同时间样品表面P/Zn 原子含量比

Table 4 Atomic ratio of P/Zn on the surfaces after immersed in AU for different time

Time / d Pure Zn Zn-0.5Li Zn-0.8Li 3 0.66±1.12 0.24±0.01 0.20±0.02 7 0.77±0.14 0.59±0.03 0.38±0.03 14 0.84±0.04 0.82±0.05 0.57±0.07 21 0.82±0.01 0.78±0.11 0.84±0.04 28 0.76±0.04 0.77±0.03 0.88±0.01