Q235钢在氧化性含Cl气氛中的高温腐蚀行为
陈土春1, 向军淮1(
), 江龙发2, 熊剑3, 白凌云1, 徐勋虎1, 徐鑫成1
), 江龙发2, 熊剑3, 白凌云1, 徐勋虎1, 徐鑫成1
High-temperature Corrosion Behavior of Q235 Steel in Oxidizing Atmosphere Containing Chlorine
CHEN Tuchun1, XIANG Junhuai1(), JIANG Longfa2, XIONG Jian3, BAI Lingyun1, XU Xunhu1, XU Xincheng1
), JIANG Longfa2, XIONG Jian3, BAI Lingyun1, XU Xunhu1, XU Xincheng1
图5. Q235钢在500和600 ℃腐蚀64 h后的截面形貌及600 ℃腐蚀64 h后的EDS谱及元素分析
Fig.5. Cross section image of Q235 steel after corrosion at 500 ℃ (a) and 600 ℃ (b) for 64 h, EDS analysis results of point A (c) and point B (d) in Fig.5b and Cl (e), Fe (f) and O (g) distrbution after corrosion at 600 ℃ for 64 h