Hydrogen Absorption Behavior of Near α Ti70 Alloy
WANG Jia1, LIU Xiaoyong1(), GAO Lingqing1,2, ZHA Xiaoqin1,2, LUO Xianfu1, ZHANG Wenli1, ZHANG Hengkun1
), GAO Lingqing1,2, ZHA Xiaoqin1,2, LUO Xianfu1, ZHANG Wenli1, ZHANG Hengkun1
图1. 不同温度退火后的试样金相组织
Fig.1. Metallographic structures of Ti70 sample after heat treatment at different temperatures: (a, b) original plate, (c, d) kept at 800 ℃ for 20 min and air-cooled to room temperature, (e, f) kept at 900 ℃ for 20 min and air-cooled to room temperature, (g, h) kept at 1000 ℃ for 20 min and air-cooled to room temperature