含硫化物夹杂的铁基非晶合金点蚀规律
张浩然1, 吴鸿燕2, 王善林1(
), 左瑶1, 陈玉华1, 尹立孟3
), 左瑶1, 陈玉华1, 尹立孟3
Pitting Behavior of Fe-based Amorphous Alloy with Sulfide Inclusion
ZHANG Haoran1, WU Hongyan2, WANG Shanlin1(), ZUO Yao1, CHEN Yuhua1, YIN Limeng3
), ZUO Yao1, CHEN Yuhua1, YIN Limeng3
图6. 在4 mol/L浓度下浸泡1 h后铁基非晶合金微观形貌分析
Fig.6. TEM morphologies of the inclusion area before the immersion (a), TEM morphologies of the inclusion area and the calibration of electron diffraction pattern of the inclusion in the area B after the immersion (b), line scan analysis result of the inclusion in the direction A (c) and EDS analysis result of the inclusion in the area B (d) of the Fe-based amorphous alloy after the immersion in 4 mol/L FeCl2 solution for 1 h