Pitting Behavior of Fe-based Amorphous Alloy with Sulfide Inclusion
ZHANG Haoran1, WU Hongyan2, WANG Shanlin1(), ZUO Yao1, CHEN Yuhua1, YIN Limeng3
), ZUO Yao1, CHEN Yuhua1, YIN Limeng3
图5. 铁基非晶合金在不同浓度FeCl2溶液中浸泡后的腐蚀形貌
Fig.5. Corrosion morphologies of the Fe-based amorphous alloy after immersion for 0 d (a, e, i, m), 3 d (b, f, j, n), 9 d (c, g, k, o) and 15 d (d, h, l, p) in FeCl2 solutions with 0.5 mol/L (a~d), 1 mol/L (e~h), 2 mol/L (i~l) and 4 mol/L (m~p)