3种热喷涂涂层在模拟气氛/煤灰环境下的热腐蚀及失效行为
Hot Corrosion and Failure Behavior of Three Thermal Spraying Coatings in Simulated Atmosphere/Coal Ash Environment
3种热喷涂涂层在模拟气氛/煤灰环境下的热腐蚀及失效行为 |
| 熊义, 刘光明, 占阜元, 毛晓飞, 罗钦, 洪嘉, 倪进飞, 刘永强 |
|
Hot Corrosion and Failure Behavior of Three Thermal Spraying Coatings in Simulated Atmosphere/Coal Ash Environment |
| XIONG Yi, LIU Guangming, ZHAN Fuyuan, MAO Xiaofei, LUO Qin, HONG Jia, NI Jinfei, LIU Yongqiang |
| 图6 热喷涂涂层的腐蚀和失效模型 |
| Fig.6 Corrosion and failure model of thermal spray coating for oxide film formation (a), alkaline melting (b) and corrosion expansion (c, d) |
|
|