3种热喷涂涂层在模拟气氛/煤灰环境下的热腐蚀及失效行为
Hot Corrosion and Failure Behavior of Three Thermal Spraying Coatings in Simulated Atmosphere/Coal Ash Environment
3种热喷涂涂层在模拟气氛/煤灰环境下的热腐蚀及失效行为 |
| 熊义, 刘光明, 占阜元, 毛晓飞, 罗钦, 洪嘉, 倪进飞, 刘永强 |
|
Hot Corrosion and Failure Behavior of Three Thermal Spraying Coatings in Simulated Atmosphere/Coal Ash Environment |
| XIONG Yi, LIU Guangming, ZHAN Fuyuan, MAO Xiaofei, LUO Qin, HONG Jia, NI Jinfei, LIU Yongqiang |
| 图2 试样在750 ℃腐蚀200 h后宏观表面形貌图 |
| Fig.2 Macroscopic surface morphologies of the sample after corrosion at 750 ℃ for 200 h: (a) T91, (b) 45CT, (c) NiCr/Cr3C2, (d) NiCrAlY |
|
|