Zr含量对Mg-3Zn-1Y合金显微组织和腐蚀行为的影响
黄涛1,2, 许春香1(
), 杨丽景2, 李福霞1,2, 贾庆功1, 宽军1, 张正卫1, 武晓峰1, 王中琪1,2
), 杨丽景2, 李福霞1,2, 贾庆功1, 宽军1, 张正卫1, 武晓峰1, 王中琪1,2
Effect of Zr Addition on Microstructure and Corrosion Behavior of Mg-3Zn-1Y Alloys
HUANG Tao1,2, XU Chunxiang1(), YANG Lijing2, LI Fuxia1,2, JIA Qinggong1, KUAN Jun1, ZHANG Zhengwei1, WU Xiaofeng1, WANG Zhongqi1,2
), YANG Lijing2, LI Fuxia1,2, JIA Qinggong1, KUAN Jun1, ZHANG Zhengwei1, WU Xiaofeng1, WANG Zhongqi1,2
图5. 不同Zr含量Mg-3Zn-1Y合金在Hank's溶液中浸泡240 h后的腐蚀形貌
Fig.5. Corrosion morphologies of Mg-3Zn-1Y(a), Mg-3Zn-1Y-0.2Zr (b), Mg-3Zn-1Y-0.4Zr (c) and Mg-3Zn-1Y-0.6Zr (d) alloys after immersion in the Hank's solution for 240 h