淡水舱涂层在不同水环境中的失效行为研究
曹京宜1, 杨延格2(
), 方志刚1, 寿海明3, 李亮1, 冯亚菲1, 王兴奇2, 褚广哲1, 赵伊1
), 方志刚1, 寿海明3, 李亮1, 冯亚菲1, 王兴奇2, 褚广哲1, 赵伊1
Failure Behavior of Fresh Water Tank Coating in Different Water
CAO Jingyi1, YANG Yange2(), FANG Zhigang1, SHOU Haiming3, LI Liang1, FENG Yafei1, WANG Xingqi2, CHU Guangzhe1, ZHAO Yi1
), FANG Zhigang1, SHOU Haiming3, LI Liang1, FENG Yafei1, WANG Xingqi2, CHU Guangzhe1, ZHAO Yi1
图2. 盐水和饮用水浸泡环境下拉拔测试后淡水舱涂层典型的宏观形貌
Fig.2. Macr-morphologies of the coating after adhesion test with immersion in salt water (a) and drinking water (b) at 0 h (a1, b1), 240 h (a2, b2), 480 h (a3, b3), 720 h (a4, b4) and 1200 h (a5, b5)