表3 充氢前后304不锈钢拉伸实验结果

Table 3 Tensile test results of 304 stainless steel before and after hydrogen charging

Condition A / % IHE(δ) / % H-free 56 --- 20 mA/cm2, 24 h 52 7.14 50 mA/cm2, 48 h 50 10.71 100 mA/cm2, 96 h 50 10.71